Multi-layer substrates comprising sandwich layers and polyethylene

ABSTRACT

Multi-layer substrates comprising a top surface layer of pulp fibers, a bottom surface layer of pulp fibers, and a melted thermoplastic material layer between the pulp fiber layers, where the thermoplastic material comprises polyethylene or has a tan delta value of 0.2 to 0.4 within the temperature range of 100° F. to 350° F. The multi-layer substrate can include a cleaning composition loaded onto the multi-layer substrate, where a fluid pathway through the melted thermoplastic material allows the cleaning composition to travel from the top surface layer to the bottom surface layer. The multi-layer substrate may be void of chemical adhesives, where adhesion between the top surface layer and the thermoplastic layer, and between the bottom surface layer and the thermoplastic layer is instead provided by the thermoplastic material itself, which bonds to groups of fibers in the pulp fibers top and bottom surface layers that are in contact with the thermoplastic material as it melts.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of U.S. patent application Ser. No. 16/710,774, filed Dec. 11, 2019, which claims the benefit of each of U.S. Provisional Patent Application No. 62/860,655, filed on Jun. 12, 2019, U.S. Provisional Patent Application No. 62/828,301, filed Apr. 2, 2019 and U.S. Provisional Patent Application No. 62/784,274 filed on Dec. 21, 2018. The disclosure of each of the foregoing is herein incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION 1. The Field of the Invention

The present invention relates to cleaning wipes, more particularly to pre-moistened cleaning wipes that are formed from multi-layer substrates.

2. Description of Related Art

Numerous cleaning wipes are available, e.g., such as CLOROX DISINFECTING WIPES. While such wipes provide good overall cleaning and disinfection characteristics, versatility, and convenience, there is a continuing need for improved cleaning wipes, as well as methods for their manufacture.

BRIEF SUMMARY

The present invention relates to wipes that may typically be pre-moistened during manufacture, where the wipe includes a multi-layer substrate comprising two or more layers, in which the wipe as a whole (on a dry basis) comprises greater than 70% by weight pulp fibers (e.g., 75% to 90% pulp fibers). By forming the vast majority of the substrate from pulp, the resulting wipe is more sustainably sourced, while potentially providing a simpler manufacturing process, and potentially offering improvements in the dosing characteristics and/or efficacy provided by the wipe. Various other fibrous nonwovens, such as meltblown, spunbond, spunlaid, SMS (spunbond-meltblown-spunbond), coform, airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, spunlace, hydroentangled, needled, chemically bonded, or combinations thereof may also be used.

An embodiment may be directed to a multi-layer substrate (e.g., a wipe) including a top surface layer that consists essentially of pulp fibers formed by at least one of the following processes: airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, hydroentangled, needled, chemically bonded, or pulp fibers, such as tissue paper (e.g., no significant load of synthetic fibers therein), a melted thermoplastic material comprising polyethylene (e.g., where the melted thermoplastic material layer is configured a thin film layer), a bottom surface layer that consists of any of the materials listed relative to the top layer (e.g., similar or identical to the top layer), and a cleaning composition loaded onto the multi-layer substrate. Because the thermoplastic layer at the interior of the “sandwich” structure has been melted, there is a fluid pathway provided through the melted thermoplastic material layer, which allows the cleaning composition to travel from the top surface layer to the bottom surface layer, through the fluid pathway of the thermoplastic material layer. The multi-layer substrate may be void of any chemical adhesives, including but not limited to: water based adhesives, hot melt adhesives, tackifying agents or resins, waxes, plasticizers, and the like, for holding the plurality of layers together. Binders may technically be present in a tissue paper or other pulp layers (e.g., in relatively small amounts) because such binders are frequently used in processing pulp material layers, although the purpose of such included binders, like kymene (PAE), is to impart strength to the pulp fibers during processing to create the pulp layer, rather than for any purpose of actually adhering a layer of pulp material to a thermoplastic material layer. Instead, the melted thermoplastic material bonds to groups of fibers (e.g., pulp fibers) in the top and bottom layers which were in contact with the thermoplastic material as it melted.

Another embodiment is directed to a multi-layer substrate comprising a top surface layer consisting essentially of at least one of: airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, spunlace, hydroentangled, needled, chemically bonded, or pulp fibers, e.g., tissue paper, a bottom surface layer consisting essentially of at least one of airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, spunlace, hydroentangled, needled, chemically bonded, or pulp fibers, e.g., tissue paper, and a melted thermoplastic material layer between the top and bottom pulp layers, where the thermoplastic material has a tan delta value of 0.2 to 0.4 within the temperature range of 100° F. to 350° F. The multi-layer substrate can also include a cleaning composition loaded onto the multi-layer substrate, where a fluid pathway through the melted thermoplastic material allows the cleaning composition to travel from the top surface layer to the bottom surface layer. The multi-layer substrate may be void of chemical adhesives, where adhesion between the top surface layer and the thermoplastic layer, and between the bottom surface layer and the thermoplastic layer is instead provided by the thermoplastic material itself, which bonds to groups of fibers in the top and bottom layers that are in contact with the thermoplastic material as it melts.

The referenced tan delta value is defined as the ratio of viscous modulus divided by elastic modulus. It therefore provides information relative to the ratio of a material's viscous liquid phase stiffness or flow characteristics relative to the material's solid phase stiffness characteristics. Different polymeric materials exhibit different tan delta characteristics, and this ratio also varies for a given material with temperature. Polyethylene is an exemplary material that exhibits a tan delta value in a range of 0.2 to 0.4 within the temperature range of 100° F. to 350° F. Other polymeric materials (e.g., polypropylene) do not necessarily exhibit such characteristics. Applicant has found that tan delta is a good indicator of whether a given polymeric material will result in a melted thermoplastic “sandwich” layer that effectively bonds to the nonwoven layers both above and below the thermoplastic inner “sandwich” layer, while at the same time opening up fluid pathways through the thermoplastic layer, allowing liquids (e.g., a cleaning composition) to flow between the top and bottom layers, through the thermoplastic layer.

Another embodiment relates to a method of manufacturing a multi-layer substrate, including providing both top and bottom surface layers, e.g., each consisting essentially of any of the nonwovens identified above, providing a thermoplastic film material layer (e.g., initially impervious to liquid) that comprises polyethylene and/or has a tan delta value of 0.2 to 0.4 within the temperature range of 100° F. to 350° F., and heating the film material layer to a temperature at which the thermoplastic film material softens, opening pores through the film or breaks in the film, so as to provide a fluid pathway through the thermoplastic film layer so that any liquid loaded onto the top surface layer is able to pass through the fluid pathway, to the bottom surface layer. Once so formed, the multi-layer substrate can be loaded with a cleaning composition, e.g., by applying the cleaning composition to the top and/or bottom surface layer(s). Because of the fluid pathway, fluid communication is possible from one surface layer to the other, through the fluid pathway in the thermoplastic film layer.

During such manufacturing, pressure can be applied with the application of heat during formation of the fluid pathway through the thermoplastic material. The application of heat, and optional application of pressure at the same time, may serve to bond the thermoplastic material to groups of fibers in the top and bottom layers that are in contact with the thermoplastic material as it softens, such that no chemical adhesives are used to adhere the top and bottom layers to the thermoplastic material.

Further features and advantages of the present invention will become apparent to those of ordinary skill in the art in view of the detailed description of preferred embodiments below.

BRIEF DESCRIPTION OF THE DRAWINGS

To further clarify the above and other advantages and features of the present invention, a more particular description of the invention will be rendered by reference to specific embodiments thereof which are illustrated in the drawings located in the specification. It is appreciated that these drawings depict only typical embodiments of the invention and are therefore not to be considered limiting of its scope. The invention will be described and explained with additional specificity and detail through the use of the accompanying drawings.

FIGS. 1A-1D show schematic views of exemplary multi-layer substrate textures with various dot patterns.

FIG. 1E is a photograph showing 4 different exemplary multi-layer substrate textures that were actually formed, each with differently sized unbonded raised texture features (i.e., raised dots).

FIG. 2 is an SEM image of the top surface of an exemplary multi-layer substrate, showing two adjacent unbonded raised regions, with the bonded region extending there-between.

FIG. 3 shows an SEM image of an cross-sectional or edge view through an exemplary multi-layer substrate such as that of FIG. 2 , showing the pulp fiber top surface layer, the pulp fiber bottom surface layer, and the thermoplastic film layer sandwiched there-between, where there are both bonded regions, and regions in which the thermoplastic layer and the adjacent pulp fiber surface layer are unbonded relative to one another.

FIG. 4 is a chart showing elastic modulus and tan delta values versus temperature for polyethylene, polypropylene, and for a polymer comprised of “bicomponent” fibers, i.e., a (“bico”) polymer.

FIGS. 5A-5B illustrate various exemplary wipes packages, showing how the present multi-layer substrate wipes can be pulled through a typical wipe pack orifice, without significant shredding of the exterior pulp fibers layers.

FIG. 6 is an SEM image showing spunbond thermoplastic fibers enveloping adjacent pulp fibers of the adjacent top surface layer.

FIGS. 7A-7F illustrate additional exemplary textures and patterns.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS I. Definitions

Before describing the present invention in detail, it is to be understood that this invention is not limited to particularly exemplified systems or process parameters that may, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments of the invention only, and is not intended to limit the scope of the invention in any manner.

All publications, patents and patent applications cited herein, whether supra or infra, are hereby incorporated by reference in their entirety to the same extent as if each individual publication, patent or patent application was specifically and individually indicated to be incorporated by reference.

The term “comprising” which is synonymous with “including,” “containing,” or “characterized by,” is inclusive or open-ended and does not exclude additional, unrecited elements or method steps.

The term “consisting essentially of” limits the scope of a claim to the specified materials or steps “and those that do not materially affect the basic and novel characteristic(s)” of the claimed invention.

The term “consisting of” as used herein, excludes any element, step, or ingredient not specified in the claim.

It must be noted that, as used in this specification and the appended claims, the singular forms “a,” “an” and “the” include plural referents unless the content clearly dictates otherwise. Thus, for example, reference to a “surfactant” includes one, two or more surfactants.

Unless otherwise stated, all percentages, ratios, parts, and amounts used and described herein are by weight.

Numbers, percentages, ratios, or other values stated herein may include that value, and also other values that are about or approximately the stated value, as would be appreciated by one of ordinary skill in the art. As such, all values herein are understood to be modified by the term “about”. Such values thus include an amount or state close to the stated amount or state that still performs a desired function or achieves a desired result. A stated value should therefore be interpreted broadly enough to encompass values that are at least close enough to the stated value to perform a desired function or achieve a desired result, and/or values that round to the stated value. The stated values include at least the variation to be expected in a typical manufacturing or other process, and may include values that are within 10%, within 5%, within 1%, etc. of a stated value.

Some ranges may be disclosed herein. Additional ranges may be defined between any values disclosed herein as being exemplary of a particular parameter. All such ranges are contemplated and within the scope of the present disclosure.

In the application, effective amounts are generally those amounts listed as the ranges or levels of ingredients in the descriptions, which follow hereto. Unless otherwise stated, amounts listed in percentage (“%'s”) are in weight percent (based on 100% active) of any composition.

The phrase ‘free of’ or similar phrases if used herein means that the composition or article comprises 0% of the stated component, that is, the component has not been intentionally added. However, it will be appreciated that such components may incidentally form thereafter, under some circumstances, or such component may be incidentally present, e.g., as an incidental contaminant.

The phrase ‘substantially free of’ or similar phrases as used herein means that the composition or article preferably comprises 0% of the stated component, although it will be appreciated that very small concentrations may possibly be present, e.g., through incidental formation, contamination, or even by intentional addition. Such components may be present, if at all, in amounts of less than 1%, less than 0.5%, less than 0.25%, less than 0.1%, less than 0.05%, less than 0.01%, less than 0.005%, less than 0.001%, or less than 0.0001%. In some embodiments, the compositions or articles described herein may be free or substantially free from any specific components not mentioned within this specification.

As used herein, “disposable” is used in its ordinary sense to mean an article that is disposed or discarded after a limited number of usage events, preferably less than 25, more preferably less than about 10, and most preferably after a single usage event. The wipes disclosed herein are typically disposable.

As used herein, the term “substrate” is intended to include any material that is used to clean an article or a surface. Examples of cleaning substrates include, but are not limited to, wipes, mitts, pads, or a single sheet of material which is used to clean a surface by hand or a sheet of material which can be attached to a cleaning implement, such as a floor mop, handle, or a hand held cleaning tool, such as a toilet cleaning device. The term “substrate” is also intended to include any material that is used for personal cleansing applications. These substrates can be used for hard surface, soft surface, and personal care applications. Such substrates may typically be in the form of a wipe.

Such substrates may be formed of a structure of individual fibers which are interlaid, typically in a manner that is not identifiable, similar to a nonwoven. The top and bottom surface layers or pulp layers included in the present substrates may be formed by any suitable process, typically through wetlaying, although airlaying may also be possible. Various processes for forming various other nonwovens will be apparent to those of skill in the art, many of which are described in U.S. Pat. No. 7,696,109, incorporated herein by reference in its entirety. Pulp fibers may generally be ribbon-shaped, rather than the generally circular fiber geometry of synthetic fibers commonly used in synthetic nonwovens, and which may be present in the thermoplastic layer of the present substrates. The thermoplastic layer may be provided as a synthetic nonwoven, formed according to any desired process. The thermoplastic layer may also be a film, rather than being comprised of fibers. The basis weight of any of the multiple layers of the substrate may be expressed in grams per square meter (gsm). Basis weight of such substrates is often also expressed in “pounds” (e.g., referring to lbs/3000 ft² of the tissue paper).

The terms “wipe”, “substrate” and the like may thus overlap in meaning, and while “wipe” may typically be used herein for convenience, it will be appreciated that this term may often be interchangeable with “substrate”.

As used herein, “wiping” refers to any shearing action that the wipe undergoes while in contact with a target surface. This includes hand or body motion, substrate-implement motion over a surface, or any perturbation of the substrate via energy sources such as ultrasound, mechanical vibration, electromagnetism, and so forth.

The cleaning compositions dosed onto the substrate as described herein may provide sanitization, disinfection, or sterilization, other cleaning, or other treatment. As used herein, the term “sanitize” shall mean the reduction of “target” contaminants in the inanimate environment to levels considered safe according to public health ordinance, or that reduces a “target” bacterial population by significant numbers where public health requirements have not been established. By way of example, an at least 99% reduction in bacterial population within a 24 hour time period is deemed “significant.” Greater levels of reduction (e.g., 99.9%, 99.99%, etc.) are possible, as are faster treatment times (e.g., within 10 minutes, within 5 minutes, within 4 minutes, within 3 minutes, within 2 minutes, or within 1 minute), when sanitizing or disinfecting.

As used herein, the term “disinfect” shall mean the elimination of many or all “target” pathogenic microorganisms on surfaces with the exception of bacterial endospores.

As used herein, the term “sterilize” shall mean the complete elimination or destruction of all forms of “target” microbial life and which is authorized under the applicable regulatory laws to make legal claims as a “sterilant” or to have sterilizing properties or qualities. Some embodiments may provide for at least a 2 or more log reduction (e.g., 3-log reduction, or 6-log reduction) in a bacterial population within a designated time period (e.g., 10 minutes, 5 minutes, 4 minutes, 3 minutes, 1 minute, 30 seconds, 10 seconds or the like). A 2-log reduction is equivalent to a 99% reduction, a 3-log reduction is equivalent to at least a 99.9% reduction, a 4-log reduction is equivalent to at least a 99.99% reduction, a 5-log reduction is equivalent to at least a 99.999% reduction, etc. An example of a target microbe may be Staphylococcus aureus. It will be appreciated that microefficacy can also be achieved against other target microbes, numerous examples of which will be apparent to those of skill in the art. It will also be appreciated that the present cleaning compositions need not include an antimicrobial agent, where sanitization or disinfection is not necessarily desired.

The term “texture” as used herein refers to the character or appearance of a substrate as determined by the arrangement and thickness of its constituent fibers. In at least some instances, texture can be quantified using imaging techniques and/or caliper measurements at the local and macro scales, as described in Applicant's application Ser. No. 16/042,690, filed Jul. 23, 2018, herein incorporated by reference in its entirety. By way of explanation, “patterns” are typically visual, with areas of discernable contrast. “Texture” is typically tactile, and relates to variations relative to the normal plane of the substrate (i.e., 3-dimensional texture in the substrate). Visual pattern and tactile texture interact in a complex manner with a user's visual/tactile sense of sight and touch to produce a given aesthetic perception for a given substrate, in addition to other quantifiable technical characteristics associated with such.

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the invention pertains. Although a number of methods and materials similar or equivalent to those described herein can be used in the practice of the present invention, the preferred materials and methods are described herein.

II. Introduction

In an aspect, the present invention is directed to multi-layer substrates including at least 3 layers, in which the exterior faces of the wipe are provided (e.g., exclusively) by structured plant based fibers, such as structured wood pulp fibers (e.g., tissue paper, conventional paper, paper towels etc.), or at least one of meltblown, spunbond, spunlaid, SMS (spunbond-meltblown-spunbond), coform, airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, spunlace, hydroentangled, needled, or chemically bonded, fibers. Wetlaid materials include both nonwoven materials as well as materials made in papermaking processes, such as tissue paper, conventional paper, etc. Where used, the term “tissue” is used for convenience, and it will be appreciated that it is intended to be broadly construed, including tissue paper materials, as well as other similar materials formed from pulp. An interior “sandwich” layer comprising a thermoplastic material is provided, between the tissue or other pulp layers (or other top and bottom layers), which adheres the entire multi-layer substrate together in a single mass, with low risk of delamination, while providing desired characteristics relative to hand-feel, stiffness, absorbency (ability to load the substrate to a desired loading ratio with a cleaning composition), while also providing a fluid pathway through the thermoplastic layer through which the cleaning composition can migrate from the top pulp fiber layer, to the bottom pulp fiber layer, or vice versa. Because the thermoplastic layer melts in contact with pulp fibers of the adjacent tissue or other pulp layers, and particularly given the tan delta characteristics of the thermoplastic material, the melt softened thermoplastic material encapsulates, envelops, wraps, or otherwise coats individual adjacent pulp fibers of the tissue layer, providing a strong bond between the two adjacent layers, such that delamination does not readily occur. In addition, the thermoplastic layer typically does not penetrate through the tissue or other pulp layers, so that no synthetic fibers or synthetic layer material is on the exposed exterior faces of the wipe. This results in the advantage that relatively softer pulp fibers are used for wiping and cleaning versus contact with harder more abrasive synthetic fibers. The wipe is thus less harsh on the surfaces being treated and does not cause any mechanical scratching, abrasion, or erosion.

Such multi-layer substrates may be formed through a thermal and pressure calendaring process in which top and bottom surface pulp fiber layers are provided (e.g., the tissue or other layers are provided preformed), and a thermoplastic film layer comprising polyethylene or another polymer having suitable tan delta values is also provided. Many commercially available multi-layer hard surface cleaning substrates have external layers made of thermoplastic materials such as polyethylene, polypropylene, PET, and other suitable synthetic materials. Typically, a layer of pulp fibers is positioned in the middle of the synthetic material layers so that the pulp fibers are not lost through abrasion during the cleaning process. In contrast, an embodiment of the present invention has the opposite configuration where the layers of pulp materials are in a top surface layer and a bottom surface layer and the thermoplastic material is between the pulp material layers.

The layers may be assembled (e.g., with the tissue layers as “bread” sandwiching the thermoplastic film layer (as “cheese”) therebetween), followed by subjecting the assembly to heat (and typically pressure) at a temperature that melt softens the thermoplastic material. This heating opens pores through the thermoplastic film, e.g., even if the film was initially impervious to liquid, while also softening the thermoplastic material so that it wraps around or otherwise coats the adjacent pulp fibers of the top and bottom tissue layers, effectively tying the adjacent layers to one another, without any chemical adhesive to prevent the layers from delaminating or pulling apart from one another. At the same time that this layer bonding occurs, any impervious film characteristics that previously existed with respect to the thermoplastic layer are broken, so that a fluid pathway is created through the thermoplastic layer, through which a cleaning composition or other liquids applied to either the top or bottom tissue layer can penetrate from one tissue layer to the other tissue layer, through the thermoplastic film layer.

Once the dry substrate has been formed, a desired cleaning composition may be loaded onto the multi-layer substrate. Because of the presence of the fluid pathway, even if the cleaning composition is loaded as a liquid only one of the top or bottom layers, it will flow through the substrate to the other exterior layer through the broken thermoplastic film layer.

III. Exemplary Multi-Layer Substrates

FIGS. 1A-1D illustrate exemplary wipes 100 a-100 d, each with a different applied surface texture and bonding pattern, but where each is configured as a multi-layer substrate including a melted thermoplastic film layer sandwiched between top and bottom pulp fiber layers. While shown with various textures, it will be appreciated that numerous other textures could be provided, or perhaps no texture at all. Additional exemplary textures are shown in FIGS. 7A-7F. FIG. 1E shows photographs of 4 exemplary multi-layer wipes 100 a-100 d that were actually manufactured for evaluation.

FIG. 2 shows a close up of one of the raised ridges 102 of one of the exemplary wipes, showing how the raised circular ridge 102 (a “dot”) is unbonded to the thermoplastic film layer disposed therebelow, such that there is actually a gap there-between, at the ridge 102. The region 104 surrounding the raised ridge 102 is bonded (and is so labeled) to the underlying thermoplastic film layer disposed therebelow. Depending on the particular applied textured pattern, the bonded region 104 may be contiguous, as shown (i.e., there is a single contiguous bonded region, rather than multiple bonded regions that are fully separated from one another). In other words, by “contiguous”, one can reach any particular location in the bonded region from any other particular location in the bonded region, by traversing only other bonded regions, without any need to traverse an unbonded region. The bonded region 104 may thus be contiguous, even though it does not cover the entire top exterior face (or bottom exterior face) of the wipe, because there are spaced apart unbonded regions 102. Stated another way, by analogy, the unbonded regions may be configured as “islands” in a “sea” of the bonded region. It will be appreciated that other configurations are of course possible.

The texture may be an embossed texture that is applied during a thermal calendaring or other manufacturing operation that laminates the 3 layers of the “sandwich” structure together. Alternatively, the texture could have been introduced into the substrate structure as a result of the geometry used in the forming screen used during the tissue making process, when depositing the pulp fibers that make up the tissue layer(s).

From FIG. 2 , it is apparent that the pulp fibers of the top surface layer (as well as the bottom surface layer) are ribbon shaped, rather than being generally circular in cross-section, as is the case with typical synthetic fibers of non-woven substrates. Such ribbon-shaped fibers rather have a generally rectangular cross-section, as opposed to being circular in cross-section. FIG. 3 is an SEM image of an end or cross-section through an exemplary multi-layer substrate, such as that of FIG. 2 , showing the thermoplastic film layer 106 (labeled “Bico”) sandwiched between a through-air-dried (“TAD”) pulp fiber top surface layer 108 a, and a TAD pulp fiber bottom surface layer 108 b. Also labeled in FIG. 3 is a bonded region 104, as well as an unbonded region, adjacent a raised ridge “dot” of the bottom pulp fiber layer 108 b. In this labeled unbonded region, there is a gap between the thermoplastic layer 106 and the bottom pulp fiber layer 108 b. While in this region the bottom pulp fiber layer 108 b is unbonded, in this same region, the thermoplastic layer 106 may (or may not be) bonded to the top pulp fiber layer 108 a. In other words, the unbonded characteristic may apply to one or both faces of the thermoplastic layer.

a. Pulp Characteristics

The fibrous portion of the top and bottom surface layers of the multi-layer substrates may be formed predominantly, and in an embodiment entirely, from pulp fibers, e.g., wood pulp or other plant fibers. Even where the thermoplastic layer is clearly not comprised of such pulp fibers (as it is instead a synthetic thermoplastic polymeric material, (e.g., having particular tan delta value characteristics), the substrate as a whole is one in which a majority of the fiber weight of the substrate is pulp. For example, greater than 70% (by weight) of the fibers of the substrate may be pulp fibers. In an embodiment 75% to 90%, 75% to 85%, or 75% to 80% of the fibers in the substrate may be pulp fibers, by weight. In other words, synthetic fibers may account for less than 30%, such as 10% to 25%, 15% to 25%, or 20% to 25% by weight of the fibers. Such is the case where the thermoplastic film layer is a fibrous film (e.g., a thin spunbond film). It will be appreciated that in another embodiment, the thermoplastic film may not necessarily be fibrous, e.g., such as in the case of a cast or “bubble” blown film that is not made up of numerous fibers, but is simply a continuous thin (e.g., cast) sheet. In such an embodiment, the thermoplastic material may still account for less than 30%, 10% to 25%, 15% to 25%, or 20% to 25% of the dry substrate, but may simply be in non-fibrous form (e.g., a cast sheet). In such a case, technically, 100% of the fibers of the substrate may be pulp fibers.

In an embodiment, all fibers of the top surface layer and bottom surface layer may consist of or consist essentially of pulp fibers. For example, these layers may not include any synthetic fibers, or any synthetic structural components (e.g., no synthetic fillers). By forming the multi-layer substrates from a high fraction of pulp, the substrates may be more sustainably sourced, e.g., where a higher fraction of the components used are derived from sustainable sources as compared to, e.g., existing wipes formed from a blend of pulp and synthetic fibers.

The pulp fibers may typically be obtained from wood, although other possible sources of pulp are also possible, e.g., from cotton, Esparto grass, bagasse, hemp, flax, jute or the like. Combinations of more than one material may be used. Various exemplary pulp fibers may include, but are not limited to, thermomechanical pulp fibers, chemimechanical pulp fibers, chemithermomechanical pulp fibers, refiner mechanical pulp fibers, stone ground wood pulp fibers, peroxide mechanical pulp fibers, and the like. The fibers of the pulp substrate may generally comprise cellulosic fibers, which are typically hydrophilic. Such hydrophilicity differs from many synthetic fibers, which are typically hydrophobic, absent special treatment.

Additional details relative to exemplary pulp fibers are found in Applicant's application Ser. No. 16/042,690, filed Jul. 23, 2018, already herein incorporated by reference herein. Such characteristics can be specifically selected to ensure sufficient quat release, as well as other characteristics.

The top and bottom pulp fiber layers of the multi-layer substrate may have a basis weight of no more than 50 lbs, no more than 40 lbs, no more than 30 lbs, or no more than 20 lbs, at least 3 lbs, at least 5 lbs, or at least 10 lbs, such as from 7 lbs to 20 lbs, or 8 lbs to 15 lbs. Such “lbs” values refer to the weight per/3000 ft², as will be appreciated by those of skill in the art.

In an embodiment, the top and bottom pulp fiber layers do not include any added synthetic fibers, e.g., such as various polyolefins or other fibers formed from synthetic polymers, e.g., polyethylene, polypropylene, PET, PVC, polyacrylics, polyvinyl acetates, polyvinyl alcohols, polyamides, polystyrenes, or the like. While such synthetic fibers are widely used in the manufacture of nonwoven substrates, Applicant seeks to reduce the use of such non-sustainable materials, and has found that by limiting or eliminating their use in the top and bottom exterior surface layers, additional benefits can be provided. For example, the present wipes can provide functional parity, and sometimes advantages, over conventional nonwoven wipes in durability, safety for use on all surfaces, ease and convenience, ability to clean and absorb light liquid spills, ability to clean large areas effectively, and microefficacy in the case of sanitization or disinfection. Furthermore, the use of significant quantities of synthetic resins in existing pre-moistened nonwoven wipes represents a significant expense, such that cost savings, renewability and sustainability benefits, and biodegradability benefits can be achieved using pulp substrates, as described herein.

The individual layers of the top and bottom pulp fiber layers that are used in manufacturing the multi-layer substrate can be formed by any of a number of different techniques, e.g., such as any of those suitable for use in forming tissue layers. Examples include, but are not limited to wet-laying and air-laying, as well as conventional press-drying, and through-air drying techniques. Wet-laying methods are used in making both nonwoven materials and paper products, including but not limited to: conventional paper, tissues, towels, napkins, and they like. Methods of making such substrate layers will be apparent to those of skill in the art. Wet-laying processes are described in U.S. Pat. Nos. 5,246,772 and 5,238,534 to Manning. Air-laying processes are described in U.S. Patent Publication No. 2003/0036741 to Abba et al. and U.S. Patent Publication No. 2003/0118825 to Melius et al. Conventional processes by which a manufactured substrate in a wet condition is pressed to remove process water, as well as through-air-drying processes will be familiar to those of skill in the art. In an embodiment, the top and bottom tissue layers are formed by through-air-drying.

Various techniques for forming nonwoven top or bottom layers that are airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, spunlace, hydroentangled, needled, or chemically bonded will be apparent to those of skill in the art, some of which are described in U.S. Pat. No. 7,696,109, already incorporated by reference.

Where tissue layers are used, one or both of the tissue layers may comprise more than a single ply, or each may comprise only a single ply. Where multiple plies are provided, they may be adhered together, so as to have adequate peel strength, e.g., as described in Applicant's application Ser. No. 16/042,690, filed Jul. 23, 2018, already incorporated by reference. Where only a single ply is present in each of the top and bottom tissue layers, no chemical adhesive may be present anywhere in the multi-layer substrates. Where two plies are used in either or both of the tissue layers, a chemical adhesive may be present in the tissue layers (i.e., between plies), but may not be present between the thermoplastic layer and the adjacent top and bottom tissue layers.

b. Thermoplastic Layer

The present multi-layer wipes include a sandwich structure in which a thermoplastic layer is provided, on the inside of the wipe, sandwiched between the pulp fiber layers. Where no chemical adhesive is used to adhere the 3 layers into an integral, single structure that does not readily delaminate between layers, but in which the thermoplastic material itself is used for this purpose, the Applicant has found that not just any thermoplastic polymer will be suitable for such a purpose. For example, in testing various thermoplastic polymers, Applicant found that various materials, even upon heating, will not readily bond to the adjacent pulp fiber layer, but will form a very weak bond, if any at all. Such weak bonding is of course unacceptable in a multi-layer substrate to be used as a cleaning wipe, where delamination must be avoided. In the present invention, the multi-layer substrates have sufficient adhesion between the layers that they do not delaminate even when wet (e.g., allowed to soak for weeks, in storage) or when used for cleaning hard surfaces. The thermoplastic layer not only binds the multi-layer substrate together as it melts, but it also imparts strength to the exterior layers of pulp fibers or tissue paper. It is surprising that this binding of the pulp layer occurs so well that there is not any significant shredding of the exterior pulp layer, e.g., as the multi-layer substrate is pulled through a typical wipe dispensing orifice.

For example, Applicant found that while polypropylene may seem like a suitable thermoplastic material to achieve such bonding between the top and bottom pulp fiber layers separated by the thermoplastic material layer, polypropylene did not provide good bonding, but resulted in weak bonding and delamination between the 3 layers. Applicant found a key characteristic or indicator as to whether a given thermoplastic material would work, is tan delta value. Tan delta value is an engineering characteristic that can be evaluated for thermoplastic polymeric materials, and gives information relative to how much “liquid” viscous phase characteristics dominate versus “solid” elastic phase characteristics, in a given material, at a given temperature. Tan delta is simply calculated as the ratio of viscous modulus divided by elastic modulus for a given material, at a given temperature. To measure the tan delta value, strips were cut from the nonwoven materials with approximate dimensions 13 mm L×10 mm W×0.07 mm T, with the longest dimension along the machine direction. The strips were clamped into the DMA tensile fixture, and oscillated at 1 Hz while ramping up the temperature up 5 degrees C./minute.

FIG. 4 charts both tan delta and elastic modulus values for 3 tested thermoplastic materials—polyethylene, polypropylene, and a bicomponent material that comprises polyethylene. For example, the bicomponent material tested is believed to be comprised of bicomponent fibers, with a fiber core (that is not polyethylene), and an exterior coating on the core, that is polyethylene. FIG. 4 charts both elastic modulus and the tan delta value for these 3 materials over the temperature range of about 100° F. to 350° F. FIG. 4 shows how the elastic modulus (i.e., stiffness) of the polypropylene is the highest, followed by the “bico”, followed by the polyethylene, and that the stiffness of each decreases with increasing temperature.

The tan delta value for the polypropylene is very low, less than 0.2, and remains less than 0.15 at temperatures from 100° F. to over 300° F. It isn't until nearly 350° F. that the tan delta value increases somewhat, but only slightly, up to a value of about 0.15, and certainly still less than 0.2. The polyethylene tan delta value is quite different, being about 0.2 at a temperature of 100° F., and increasing to about 0.25 to 0.3 at about 175° F.-190° F. After peaking at around this temperature, the tan delta value begins to decrease, to 0.2 at about 250° F., and dropping somewhat below 0.2 (e.g., about 0.18) at about 260°-270° F. Tan delta for the “bico” is between that of the polypropylene and the polyethylene for much of the temperature range, until about 250° F. where it is higher than the polyethylene. Both the polyethylene and the “bico” material (which comprises polyethylene) include points along the temperature range of 100° F. to 350° F. where tan delta is at least 0.2 (e.g., greater than 0.2 to 0.4, or greater than 0.2 to 0.3). The polypropylene tan delta never reaches 0.2 over this temperature range of 100° F. to 350° F. Thus, in an embodiment, the selected thermoplastic material for the “sandwich” layer has a tan delta value that is at least 0.2 (e.g., from 0.2 to 0.4, or from 0.2 to 0.3) somewhere within the temperature range of 100° F. to 350° F. In an embodiment, the selected thermoplastic material may have such a tan delta value at the particular temperature at which the thermal calendaring step is performed (e.g., 150° F., 175° F., 200° F., 225° F., 250° F., 275° F., 300° F., 325° F., etc.) or at any narrower range within the temperature range of 100° F. to 350° F.

The selected thermoplastic material may advantageously have a melting temperature that is less than 400° F., less than 375° F., less than 350° F., less than 325° F., less than 300° F., at least 150° F., at least 175° F., at least 200° F., or at least 225° F. Having a relatively lower melting temperature of course reduces energy requirements needed in the calendaring process, but may also be particularly important given the use of tissue paper exterior layers, where paper ignites at 451° F. Even below such an ignition temperature, there may be undesirable changes in the tissue paper (e.g., discoloration, embrittlement, etc.). As such, selection of lower melting temperature thermoplastic materials may be preferred, so long as they can provide a good bond to the tissue layers.

FIGS. 5A-5B show how the present multi-layer substrates may be packaged within any of various exemplary flex packs (FIG. 5A), cylinders (FIG. 5B) or other containers for storage and dispensing. The wipes 100 may be pulled through an orifice such as typically provided with such containers, without fear of shredding or delamination of the various layers. In particular, Applicant tested prototype wipes such as shown in FIG. 1E by pulling them through orifices (e.g., as seen in FIGS. 5A-5B), and there was no significant shredding of the exterior tissue layers, or delamination of the layers from one another. Rather, each wipe was able to be pulled through the orifice, remaining fully intact, time after time. FIG. 6 shows an SEM image at the interface between a spunbond fibrous thermoplastic layer 106 and an adjacent exterior tissue layer (e.g., 108 a) showing how the pulp fibers at the interface are wrapped around, enveloped, or coated by the melt-softened thermoplastic material, that occurs during the thermal calendaring process. This strong connection between the pulp fiber layer and the thermoplastic layer provides a strong bond, so that shredding or delamination do not occur when pulling the wipe through a typical wipe pack orifice. These characteristics are believed to result because of the tan delta characteristics of the thermoplastic material described above in conjunction with FIG. 4 .

FIG. 5B further shows how such wipes may be packaged as a “donut”, e.g., in a cylindrical container. The ability to package the wipes in such a donut configuration is somewhat surprising, given the high pulp content (e.g., 75-80% pulp) of the substrate. For example, it is difficult to package pre-dosed 100% pulp substrates in such a configuration without the donut collapsing or creasing vertically, due to insufficient stiffness of the substrate.

The thermoplastic film layer is not required to be particularly thick. For example, the thermoplastic film layer may have a thickness of 0.01 mm to 0.1 mm, or 0.01 mm to 0.05 mm. It may be so thin as to be transparent or translucent, prior to assembly into the sandwich structure.

c. Cleaning Composition

Many cleaning composition components as known within the art may be suitable for use in the present pre-dosed wipes. In an embodiment, the cleaning composition is an aqueous composition, including at least 90% water by weight (e.g., 90% to 99% water). The composition may include 0.05% to 5% by weight of a quaternary ammonium compound, and/or 0.1% to 5% by weight of a glycol ether solvent. For example, the quaternary ammonium compound may be included from 0.05%, from 0.1%, up to 5%, up to 4%, up to 3%, up to 2%, or up to 1% by weight of the cleaning composition. The glycol ether solvent may be included from 0.1%, from 0.25%, up to 5%, up to 4%, up to 3%, up to 2%, or up to 1% by weight of the cleaning composition. Other solvents, surfactants, and various other adjuvants often included in cleaning compositions may optionally be present. While some embodiments may include lower alcohol solvents (e.g., C1-C4 alcohols), the amount of such volatile solvents may be limited, e.g., to less than 10%, less than 5%, less than 3%, less than 2%, or less than 1% by weight. In some embodiments, the composition may be free of, or substantially free of, such lower alcohol or other highly volatile solvents.

Quaternary ammonium compounds have broad spectrum antimicrobial properties. A variety of different quaternary ammonium compounds can be used in the cleaning composition. Non-limiting examples of quaternary ammonium compounds are typically halides (e.g., a chloride) of alkyldimethylbenzylammonium, alkyldimethylethylbenzylammonium, alkyldimethylammonium, or the like. The alkyl groups of such quaternary ammonium compounds may typically range from C12 to C18. Quaternary ammonium compounds are described in more detail in U.S. Pat. No. 6,825,158, incorporated by reference herein, and will already be familiar to those of skill in the art.

Organic acids can also be used to provide antimicrobial properties. By way of example, such an organic acid may be included in an amount of at least 0.1%, or at least 0.5%, up to 5%, up to 4%, up to 3%, up to 2%, or up to 1% by weight of the cleaning composition.

The cleaning composition may include a glycol ether solvent. Exemplary glycol ether solvents include, but are not limited to, ethylene glycol monopropyl ether, ethylene glycol monobutyl ether, propylene glycol n-propyl ether, propylene glycol monobutyl ether, propylene glycol t-butyl ether, diethylene glycol monoethyl or monopropyl or monobutyl ether, di- or tri-polypropylene glycol methyl or ethyl or propyl or butyl ether, acetate and/or propionate esters of glycol ethers.

Those of skill in the art will appreciate that any among a wide variety of surfactants (e.g., anionic, cationic, non-ionic, zwitterionic, and/or amphoteric) may be included in the cleaning composition, as desired. Where included, a surfactant may be present from 0.05%, from 0.1%, up to 10%, up to 5%, up to 4%, up to 3%, up to 2%, or up to 1% by weight of the cleaning composition. Various surfactants and other optional adjuvants are disclosed in U.S. Pat. No. 3,929,678 to Laughlin and Heuring, U.S. Pat. No. 4,259,217 to Murphy, U.S. Pat. No. 5,776,872 to Giret et al.; U.S. Pat. No. 5,883,059 to Furman et al.; U.S. Pat. No. 5,883,062 to Addison et al.; U.S. Pat. No. 5,906,973 to Ouzounis et al.; U.S. Pat. No. 4,565,647 to Llenado, and U.S. Publication No. 2013/0028990. The above patents and applications are each herein incorporated by reference in their entirety.

As used herein the term “liquid” and “cleaning composition” includes, but is not limited to, solutions, emulsions, suspensions and so forth. Thus, liquids may comprise and/or contain one or more of the following: disinfectants; antiseptics; diluents; surfactants, such as nonionic, anionic, cationic; waxes; antimicrobial agents; sterilants; sporicides; germicides; bactericides; fungicides; virucides; protozoacides; algicides; bacteriostats; fungistats; virustats; sanitizers; antibiotics; pesticides; and so forth. Examples of some such components are included in, but not limited to, U.S. Pat. Nos. 6,825,158; 8,648,027; 9,006,165; 9,234,165, and U.S. Publication No. 2008/003906 each of which is herein incorporated by reference in its entirety. In some embodiments, it may be possible to provide the substrates in dry form, where dosing with a selected cleaning composition may occur later (e.g., by the user).

With regard to pre-moistened substrates, a selected amount of liquid may be added to the container or wipes during manufacture such that the cleaning substrates contain the desired amount of liquid. The substrates are not necessarily loaded to their saturation point, but are typically loaded with the cleaning composition to some ratio less than full saturation. For example, many substrates are capable of holding about 8 to 14 times their weight in liquid. For reasons described herein, the substrates may be loaded at a loading ratio less than saturation, e.g., less than 6:1, less than 5:1, less than 4:1, such as from 1:1 to 4:1, from 2:1 to 4:1, from 2.5:1 to 3.5:1, from 2.5:1 to 3:1 or from 2.5:1 to 3.75:1.

d. Other Characteristics

The size and shape of the wipe can vary with respect to the intended application and/or end use of the same. The cleaning substrate can have a substantially rectangular shape of a size that allows it to readily engage standard cleaning equipment or tools such as, for example, mop heads, duster heads, brush heads, mitten shaped tools for wiping or cleaning, and so forth. In another embodiment, another shape, e.g., circular, oval, or the like) may be provided.

The wipes or other cleaning substrates may be provided pre-moistened with a cleaning composition. The wet cleaning substrates can be maintained over time in a sealable container such as, for example, within a bucket or tub with an attachable lid, sealable plastic pouches or bags, canisters, jars, and so forth. Desirably the wet, stacked cleaning substrates are maintained in a resealable container. The use of a resealable container is particularly desirable when using aqueous volatile liquid compositions since substantial amounts of liquid can evaporate while using the first sheets thereby leaving the remaining sheets with little or no liquid. Exemplary resealable containers and dispensers include, but are not limited to, those described in U.S. Pat. No. 4,171,047 to Doyle et al., U.S. Pat. No. 4,353,480 to McFadyen, U.S. Pat. No. 4,778,048 to Kaspar et al., U.S. Pat. No. 4,741,944 to Jackson et al., U.S. Pat. No. 5,595,786 to McBride et al.; the entire contents of each of the aforesaid references are incorporated herein by reference.

Typically, the cleaning substrates are stacked and placed in the container and the liquid subsequently added thereto, all during mass manufacturing. It is advantageous that the thermoplastic layer at the center of each wipe not be liquid impervious, to facilitate easier loading of the wipes. As described herein, even if the thermoplastic film as initially provided before lamination of the 3 layers together is liquid impervious, Applicant has found that cracks or other fluid pathways are opened up within the film during thermal calendaring, as contemplated herein. While this may not necessarily occur with any and all thermal calendaring operations, it does occur under the conditions contemplated herein.

The presence of such cracks or other fluid pathways that are opened up during manufacture of the multi-layer substrate advantageously allow liquid cleaning composition dosed on either face of the substrate to migrate through the wipe, to the opposite exterior face, through the thermoplastic film layer. This similarly allows dosed cleaning composition to migrate from one substrate to the next, e.g., where the substrates are stacked (e.g., by wicking the liquid from one to the next). For example, a given volume or weight of the cleaning composition may simply be dosed into the bottom of the container, allowing it to wick into the stack of wipes. In the case of a donut configuration, by placing the cleaning composition into the bottom of the cylindrical container, an end of each wipe actually make simultaneous contact with the cleaning composition in the bottom of the container, where it can be wicked up into the height of each wipe (and the height of the donut). This may actually occur with a donut configuration whether the thermoplastic film layer were “broken” to include the described fluid pathways or not (i.e., if it remained impervious), as both the top and bottom pulp fiber layers will contact the cleaning composition at the bottom of the container simultaneously. Where any initially liquid impervious characteristics of the film are “broken” by the thermal calendaring process, this may further aid the cleaning composition in wicking upwards throughout the full height of each wipe, and the donut as a whole.

No matter the packaging and dosing process, once manufactured and packaged, the substrate can subsequently be used to wipe a surface. The moistened cleaning substrates can be used to treat various surfaces. As used herein “treating” surfaces is used in the broad sense and includes, but is not limited to, wiping, polishing, swabbing, cleaning, washing, disinfecting, scrubbing, scouring, sanitizing, and/or applying active agents thereto.

The wipes or other cleaning substrates of the present invention can be provided in a kit form, wherein a plurality of cleaning substrates and a cleaning tool are provided in a single package.

In addition to material composition and construction (e.g., tissue substrates on the exterior, thermoplastic layer only on the inside, not on the exposed face, composition of the cleaning “lotion” and the like), wipe or other substrate dimensions can also be used to control dosing as well as provide ergonomic appeal. In one embodiment, substrate dimensions are from about 5½ inches to about 11 inches in length, and from about 5½ inches to about 11 inches in width to comfortably fit in a hand. The substrate can have dimensions such that the length and width differ by no more than about 2 inches. Larger substrates may be provided that can be used and then folded, either once or twice, so as to contain dirt within the inside of the fold and then the wipe can be re-used. Such larger substrates may have a length from about 5½ inches to about 13 inches and a width from about 10 inches to about 13 inches. Such substrates can be folded once or twice and still fit comfortably in the hand.

While most synthetic or blended nonwoven substrates used in wipe manufacture exhibit significant differences in tensile strength in the machine direction (MD) versus the cross direction (CD), the present multi-layer substrates may exhibit values in each direction that result in a ratio of MD/CD that is relatively close to 1, e.g., such as 0.5 to 1.5, 0.75 to 1.25, or 0.8 to 1.2. In other words, the substrates may be substantially isotropic with respect to their tensile strength. Such substantially isotropic characteristics reduce the likelihood of there being problems when folding substrates into stacks for packaging, or forming donuts for packaging.

Various other characteristics relating to stiffness, strength, density of pulp fibers, wet bulk factor, profile height, pore volume distribution characteristics, retention characteristics, lotion retention, MABDF, and others that may be provided by the present wipes are described in Applicant's application Ser. No. 16/042,690, filed Jul. 23, 2018, already incorporated herein by reference.

e. Antimicrobial Efficacy & Other Characteristics

Exemplary multi-layer substrates were tested for their ability to effectively deliver an antimicrobial quaternary ammonium compound to a surface during simulated cleaning. Applicant notes that the generally anionic characteristics of typical pulp substrates lead to a tendency of the substrate to bind or otherwise retain the cationic quaternary ammonium compound, even when squeezing an aqueous cleaning composition including such a quat from the substrate. In other words, typically, the concentration of quaternary ammonium compound in the “squeezate” (the cleaning composition as squeezed from the pre-loaded wipe) is less than the concentration of quaternary ammonium compound in the cleaning composition before it was loaded into the wipe. Since quaternary ammonium compounds are known to bind to pulp substrates, it was unexpected that the present wipes were able to release a significant enough portion of the quaternary ammonium compound to achieve disinfectancy and/or sanitization on a treated surface without the inclusion of any biocide release agent or latex binder in the substrate. Even more surprising was that even though the tested substrate was comprised of 78% pulp fibers by weight, when compared to a blended substrate including 60% pulp fiber by weight, the present substrates exhibited greater quat release in the “squeezate” as compared to the comparative wipe, which included lower pulp content.

Because of these interesting and advantageous characteristics, there may not be a need to increase the quat concentration in the cleaning composition, in order to achieve a desired level of microefficacy, as compared to that used in the comparative wipe. For example, commercially available disinfecting wipes often contain about 0.1 to 5%, and preferably 0.1 to 3%, and more preferably 0.1 to 2% by weight of quat in the cleaning composition. Surprisingly, despite the fact that the multi-layer substrates of the present invention have higher levels of pulp they also have good microefficacy performance with 0.1 to 3%, and preferably 0.1 to 2% by weight of quat in the cleaning composition. In an embodiment, the wipes release at least 40%, at least 50%, at least 55%, at least 60%, or at least 65% of the quaternary ammonium compound (i.e., quaternary ammonium compound in the squeezate as compared to the cleaning composition before loading). The wipes may exhibit at least a 3-log reduction in a target microbe, such as Staphylococcus aureus, within a given time frame (e.g., such as 5 minutes, 4 minutes, 3 minutes, 1 minute, 30 seconds, 10 seconds, etc.).

Table 1 shows the results of testing in which a cleaning composition including a quaternary ammonium compound was loaded into a substrate according to the present invention, and as compared to a conventional blended substrate. The cleaning composition was squeezed from both substrates, and the squeezate was analyzed to determine the reduction in the concentration of the quaternary ammonium compound in the squeezate compared to the composition as loaded.

TABLE 1 Substrate % Quat Released 60/40 blended substrate- 51% comparative example 78/22 exemplary multi-layer 69% substrate

The ability to achieve higher quat release while including higher pulp content is particularly surprising and unexpected. This characteristic advantageously allows for better relative microefficacy characteristics. This high quat release may be due to the presence of absorptive pockets or gaps, e.g., such as seen in FIG. 3 , adjacent the unbonded regions. Such gaps provide a significant absorptive region between the thermoplastic film layer and the unbonded raised region 102, which can serve as a reservoir for the cleaning composition. Such regions allow significant quantities of the cleaning composition to be stored within the substrate, to be released upon squeezing, wiping, or other compression, where there is reduced contact between the quat in the composition and any anionic binding sites associated with the pulp fibers of the exterior surface layer. This combination of the reservoirs being partially bounded by the inert thermoplastic film material (which does not include significant concentration of anionic binding sites), in combination with the gaps associated with the reservoirs themselves is believed to at least partially account for the ability to release such high fractions of the quat upon squeezing the wipe.

Other characteristics of the comparative and exemplary substrates are shown in Table 2 below.

TABLE 2 60/40 blended substrate- 78/22 exemplary comparative multi-layer Characteristic example substrate Basis weight 52 gsm 55 gsm (26 lb tissue layers + 12 gsm thermoplastic layer Composition 60/40 78/22 (% pulp/% synthetic) Caliper (wet-mm) 0.6 0.76 Absorbency (g) 12 12 Tensile Strength (MD/CD-lb_(f)) 4.61/1.63 3.48/3.06 Dry Stiffness (mg · cm) 285 500 Carrier release total-S₁/S₂ (g) 0.49/0.63 0.58/0.56 Visible Pattern Snake Medium dot (100c)

By way of further explanation the dot patterns and textures shown in FIG. 1E included smallest dots (100 b), small dots (100 c), medium dots (100 a), and large dots (100 d). The wet thickness of the resulting substrates is affected by the dot pattern or texture. For example, a flat sample (not shown) had a wet thickness of 0.3 mm, the sample 100 a (smallest dots) had a wet thickness of 0.39 mm, the sample 100 b (small dots) had a wet thickness of 0.65 mm, the sample 100 c (medium dots) had a wet thickness of 0.66 mm, and sample 100 d (large dots) had a wet thickness of 0.83 mm. The forgoing values are for substrates with only one tissue layer textured. Two sided samples include somewhat higher wet thickness values.

The dosed exemplary multi-layer substrate was tested for microefficacy against Staphylococcus aureus at a loading ratio of 3.75:1, using an existing quat cleaning composition, at a contact time of 3 min 30 sec. The control population of 6.1 log was reduced to 0 in each of 60 replicates. Testing was performed under 5% soil load conditions. Such results indicated excellent efficacy against Staphylococcus aureus at a 3:30 contact time.

The dosed wipes were also tested for efficacy in various other household cleaning tasks, including cleaning kitchen grease (KG) and bathroom scum (BS). The results of such testing demonstrated parity or near parity with the comparative wipe, as shown below in Table 3.

TABLE 3 % soil % soil removal removal Cycles Cycles at 30 at 30 to 75% to 75% cycles- cycles- removal- removal- Substrate KG BS KG BS 60/40 blended 96.87 96.62 4 7 substrate- comparative example 78/22 exemplary 97.92 96.2 6 9 multi-layer substrate

The small increase in cycles for 75% removal may be due to the absence of synthetic fibers on the exterior surface and reduced tendency of the present wipes to “dump” cleaning composition, as compared to the comparative example blended wipe. The reported values represent averages for two sides of the wipes. The conventional wipe “dumps” or releases more liquid from the first side, thereby requiring few cycles to clean, but also reducing mileage. This “dumping” characteristic is described in Applicant's application Ser. No. 16/042,690, filed Jul. 23, 2018, already incorporated by reference.

As mentioned, the present wipes do not include any synthetic fibers exposed at the exterior faces of the wipe, but any synthetic fibers are rather located only within the interior of the wipe (and potentially incidentally exposed at the edges). As a result, the exterior surface may be soft, rather than abrasive. While Applicant did prepare some prototype substrates that did include synthetic fibers on the exterior surfaces (i.e., using a blend of pulp and synthetic fibers to form the exterior “tissue layers”, the resulting wipes did not provide the same desired hand-feel characteristics as were provided where the exterior pulp fiber or tissue layers did not include exposed synthetic fibers. While 100% pulp fibers on the exterior faces may thus be preferred, it will be appreciated that some small fraction of synthetic fibers (e.g., less than 10%, less than 5%, less than 3%, or less than 1%) may be included in some embodiments.

The exterior tissue layers may be of a through-air dried configuration. While conventional press-dried tissue was also tried in this exterior layer, this also resulted in less desirable hand-feel characteristics. Such conventional (not through-air-dried) tissue also undesirably presses out any initially included texture, while through-air-dried processing preserves such pre-existing texture. While these alternatives may not be preferred, they may still be suitable, for some uses. Various other possible paper, tissue or nonwoven manufacturing techniques based on dry crepe, through-air drying and combinations thereof with production equipment sold by Valmet Oyj, Voith GmbH & Co, Andritz AG, Toscotec S.p.A. and others that will be apparent to those of skill in the art may also be suitable in at least some embodiments. Other suitable tissue or nonwoven manufacturing techniques, include but are not limited to: dry crepe technique (DCT), structured tissue or new tissue technology (NTT), Valmet QRT, Voith GmbH & Co. ATMOS or Cascades ATAD, Andritz AG TEX, ETAD and others that will be apparent to those of skill in the art may also be suitable in at least some embodiments.

While use of polyethylene or another thermoplastic polymer having the described tan delta characteristics eliminates any need for a chemical adhesive to adhere the top and bottom surface layer to the thermoplastic layer, it will be appreciated that in other embodiments, e.g., even using polypropylene or another material having poor tan delta characteristics, it may be possible to achieve a multi-layer substrate that does not delaminate, e.g., by using a chemical adhesive to provide the needed bonding.

The degree of lamination and strength of the bond between adjacent layers typically depends on the temperature, pressing or contact time, and applied pressure associated with the calendaring operation. Temperature may be a primary variable responsible for bond strength achieved, although pressure and time may also have an effect, and may also affect the resulting texture that is “embossed” into the pulp fiber surface layer, and the resulting bond pattern. Where the pulp fiber layers provided on both exterior faces are embossed with a texture, the resulting multi-layer substrate exhibits a more “cloth-like” feel that is drapable and less stiff, as compared to where only one of the two faces is embossed with a texture. In addition, it was observed that all else being equal, heavier tissue (i.e., greater lb weight) produces a stiffer substrate. FIGS. 7A-7F illustrate various possible embossing patterns that can be applied by the calendar rollers. It will be apparent that the possibilities are nearly limitless.

Temperatures applied during calendaring may be at least 150° F., at least 175° F., at least 200° F., from 200° F. to 400° F., or from 200° F. to 350° F. Applied pressure may be at least 50 psi, at least 100 psi, at least 150 psi, at least 200 psi, from 100 psi to 1000 psi, or from 300 psi to 600 psi. Contact time (time at the given pressure and/or temperature) may be at least 100 ms, at least 200 ms, from 100 ms to 5 s, from 200 ms to 1 s, or from 200 ms to 500 ms.

Such a manufacturing process may be attractive, e.g., as compared to traditional non-woven substrate manufacture, as it may not require any fiber processing, water usage, water filtration, drying steps, loss of wood pulp during processing, and the like. In addition, the present calendaring process may allow for greater production line speeds (e.g., up to 900 m/min, typically from 50 m/min to 600 m/min) as compared to spinlace manufacturing conventional blended substrates (that are not multi-layer), which are at significantly lower line production speeds.

Increased line speed results in decreased contact time (all else being equal). To provide the desired good bonding, higher line speed may be accommodated by increasing web surface temperature (so shorter contact time is needed), increasing the roller diameter (thus increasing contact time), or increasing applied pressure (nip pressure). By way of example, for every 25 m/min increase in line speed, temperature can be increased by about 5% (in ° C.) to maintain bonding level).

With respect to embossed textures, it was observed that “pin” textures (e.g., associated with fine dots) can result in tearing of the top and bottom surface layers, as the fibers get caught on the pins. Thus, textures that are formed using more of a “flat bar” type contact versus a sharp “pin” may be preferred, as such larger features do not result in such tearing. In addition, it was observed that when manufacturing such substrates through a calendaring operation, that the thermoplastic “cheese” layer should be narrower in width than the top and bottom surface “bread” layers in order to further minimize complications during manufacture. From such a processed multi-layer laminated web, individual sized wipes may be cut to the desired size. Edges of the web that may not include the thermoplastic “cheese” layer could be cut away during such cutting, if desired.

The present substrates also provide for pulp reinforcement with polymeric fibers, the ability to modulate the substrate stiffness by changing the pattern applied during calendaring (e.g., see the various patterns of FIG. 1E), the ability to modulate stiffness and tensile strength characteristics by texturing on one or both of the substrate faces, the ability to provide for relatively higher quat release even at higher pulp fractions, and more uniform lotion release, with better mileage, as described in Applicant's application Ser. No. 16/042,690, filed Jul. 23, 2018, due to the high pulp content.

Without departing from the spirit and scope of this invention, one of ordinary skill can make various changes and modifications to the invention to adapt it to various usages and conditions. As such, these changes and modifications are properly, equitably, and intended to be, within the full range of equivalence of the following claims. 

The invention claimed is:
 1. A multi-layer substrate comprising: (a) a top surface layer consisting essentially of: pulp fibers formed by one of the following processes: airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, hydroentangled, or chemically bonded and any combinations thereof; (b) a middle layer comprising a thermoplastic material; (c) a bottom surface layer consisting essentially of: pulp fibers formed by one of the following processes: airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, hydroentangled, or chemically bonded and any combinations thereof; and (d) a cleaning composition loaded onto said multi-layer substrate wherein a fluid pathway through the thermoplastic material allows the cleaning composition to travel from the top surface layer to the bottom surface layer; (e) wherein the multi-layer substrate is void of any chemical adhesives, the thermoplastic material instead, when melted, bonding to groups of fibers in the top surface layer and the bottom surface layer that are in direct contact with the thermoplastic material as it melts and fractures, forming fluid pathways; and (f) wherein the thermoplastic material is initially in the form of a liquid impervious thin film, which becomes porous upon melting so as to provide the fluid pathway through which the cleaning composition is able to travel both from the top surface layer to the bottom surface layer and from the bottom surface layer to the top surface layer.
 2. The multi-layer substrate of claim 1, wherein the cleaning composition comprises a quaternary ammonium compound.
 3. The multi-layer substrate of claim 2, wherein at least 50% of a quaternary ammonium compound included in the cleaning composition loaded onto the multilayer substrate is released from the multilayer substrate to a surface being cleaned.
 4. The multi-layer substrate of claim 1, herein the cleaning composition comprises an organic acid.
 5. The multi-layer substrate of claim 1, wherein the top and bottom surface layers are wetlaid nonwoven materials selected from the following group: through-air-dried material, a press-dried tissue material, a DCT tissue material or a structured tissue material.
 6. The multi-layer substrate of claim 1, wherein the thermoplastic material of the middle layer is a film having a thickness from 0.01 mm to 0.05 mm.
 7. The multi-layer substrate of claim 1, wherein the multi-layer substrate includes: (i) unbound regions where the thermoplastic material is not bound to the adjacent fibers of the top or bottom surface layer; and (ii) bound regions where the thermoplastic material is bound to the adjacent fibers of both the top and bottom surface layer.
 8. The multi-layer substrate of claim 7, wherein the unbound regions correspond to raised texture features embossed in the top or bottom surface layer.
 9. The multi-layer substrate of claim 8, further comprising a gap associated with the unbound region in which the cleaning composition is stored.
 10. The multi-layer substrate of claim 1, wherein no adhesive is present between the thermoplastic material middle layer and the top and bottom surface layers, but rather the melted thermoplastic material directly bonds to groups of fibers in the top surface layer and the bottom surface layer, the melting and fracturing of the thermoplastic material forming an irregularly patterned bonded region between the thermoplastic material middle layer and the adjacent top and bottom surface layers.
 11. A multi-layer substrate comprising: (a) a top surface layer comprising: pulp fibers formed by one of the following processes: airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, hydroentangled, or chemically bonded and any combinations thereof; (b) a middle layer comprising a melted thermoplastic material; (c) a bottom surface layer comprising: pulp fibers formed by one of the following processes: airlaid, wetlaid, carded webs, thermal bonded, through-air bonded, thermoformed, hydroentangled, or chemically bonded and any combinations thereof; and (d) a cleaning composition loaded onto said multi-layer substrate wherein a fluid pathway through the melted thermoplastic material allows the cleaning composition to travel from the top surface layer to the bottom surface layer; (e) wherein the multi-layer substrate is void of any chemical adhesives, the thermoplastic material instead, when heated, bonding to groups of fibers in the top or bottom surface layer that are in direct contact with the middle layer comprising the thermoplastic material as it melts; and (f) wherein the melted thermoplastic material is initially in the form of a liquid impervious thin film, which becomes porous upon melting so as to provide the fluid pathway through which the cleaning composition is able to travel both from the top surface layer to the bottom surface layer and from the bottom surface layer to the top surface layer.
 12. The multi-layer substrate of claim 11, wherein the cleaning composition comprises a quaternary ammonium compound.
 13. The multi-layer substrate of claim 12, wherein at least 50% of a quaternary ammonium compound included in the cleaning composition loaded onto the multilayer substrate is released from the multilayer substrate to a surface being cleaned.
 14. The multi-layer substrate of claim 11, wherein the cleaning composition comprises an organic acid.
 15. The multi-layer substrate of claim 11, wherein the top surface layer is a wetlaid material selected from the following group: through-air-dried material, a press-dried tissue material, a DCT tissue material or a structured tissue material.
 16. The multi-layer substrate of claim 11, wherein the thermoplastic material of the middle layer is a film having a thickness from 0.01 mm to 0.05 mm.
 17. The multi-layer substrate of claim 11, wherein the thermoplastic material of the middle layer comprises polyethylene.
 18. The multi-layer substrate of claim 11, wherein the multi-layer substrate includes: (i) unbound regions where the thermoplastic material is not bound to adjacent fibers of the top or bottom surface layer; and (ii) bound regions where the thermoplastic material is bound to adjacent fibers of both the top and bottom surface layer.
 19. The multi-layer substrate of claim 18, wherein the unbound regions correspond to raised texture features embossed in the top or bottom surface layer.
 20. The multi-layer substrate of claim 19, further comprising a gap associated with the unbound region in which the cleaning composition is stored. 